The effect of the addition of Ga in NiAl alloys on the crystal structure, ageing behaviour and martensitic transformation is studied. Up to 10 at. % Ga can be dissolved in NiAl matrix. All Ni66Al33Ga1, Ni66Al30Ga4, Ni66Al24Ga10 alloys can consist of several phases, NiAl (B2), Ni3Al (<$E gamma>), martensitic phase NiAl (<$E L1 sub 0>) and Ni5Al3, depending on the thermal treatment. Two types of martensite presumably appear in NiAlGa alloys. The temperature dependence of resistance and calorimeters data reveal two kinds of peculiarities typical for these alloys. One of them is connected with the martensitic transformation undergoing at relatively low temperatures (0 - 300 <$E symbol Р>C), and the second one can be considered as high-temperature reverse martensitic transformation superimposing with the decomposition of <$E L1 sub 0> and/or B2 phase in Ni5Al3. It is supposed that the addition of Ga in NiAl alloys accelerates the processes of decomposition.

Індекс рубрикатора НБУВ: К232.204.3

Рубрики:

Структурні та фазові перетворення у нікелі та його сплавах

Шифр НБУВ: Ж14161 Пошук видання у каталогах НБУВ 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Коваль Юрій Миколайович (1939–) (фізико-математичні науки)
• Односум Валерій Владиславович (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"