The radiation hardness of Czochralski grown n-type silicon samples doped with germanium and without it was investigated after irradiation by fast neutrons. The dependence of the effective carrier concentration on fluence was described in the framework of Gossick's corrected model. It was found that doping the germanium impurity resulted in increase of n-Si radiation hardness. The isothermal annealing of <$E n- roman {Si~symbol ... Ge symbol ъ}> after fluence <$E 1,4~times~10 sup 14~roman {n symbol Р~cdot~cm sup -2}> was studied. It was shown that the annealing of defect clusters is caused by the annihilation of vacancy type defects in clusters with interstitial defects. For di-interstitial, silicon interstitial atom and vacancy the migration energies and frequency factors were determined. During the storage at room temperature, the behaviour of defect levels Ec - 0,17 eV and Ec - 0,078 eV was studied in the samples of Si (DOFZ) and <$E roman {Si~symbol ... Ge symbol ъ}>, correspondingly.

Індекс рубрикатора НБУВ: В379.227

Рубрики:

Радіаційні ефекти в напівпровідниках

Шифр НБУВ: Ж16425 Пошук видання у каталогах НБУВ 

---

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"