The optimal composition of etchant solution and etching time for chemical treatment to obtain nanoporous Si have been determined. Influence of nanocrystal dimensions on the electrophysical and photoelectrical properties of heterojunctions has been studied. The current-voltage characteristics of nanoporous Si with various nanocrystal dimensions were measured. It was ascertained that lux-ampere characteristics have a linear range and sublinear one, which almost reaches the asymptote at the intensity of light above 10,000 lux. Nanoporous Si on the substrate of Si single-crystal has increased sensitivity to the humidity in comparison with that of metallurgical Si. The obtained results can be applied for development of highly sensitive sensors of humidity.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Свеженцова Катерина Віталіївна (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"