It is determined that the dependences of hardness on the structure element size for single-phase L12 intermetallide and eutectic (<$E roman L1 sub 2~+~beta>) alloy of the ternary Al - Ti - Cr system follow the Hall-Petch relation. For these alloys, the values of <$E sigma sub omicron> and <$E k sub y> are defined, starting from which the values of structure parameters needed to achieve the ductile behaviour upon compression and tension are found in conformity with the Cottrell criterion for the brittle-ductile transition. For the achievement of plasticity under tension of the eutectic alloy, the structure element size (the thickness of plates in eutectic) must be diminished more than by 6 times (less than 700 nm). For the achievement of plasticity under tension of the single-phase alloy, the grain size must be smaller than 130 nm, i.e. it must be diminished more than by 100 times.

• Мільман Юлій Вікторович (1930–2021) (фізико-математичні науки)
• Коржова Наталія Петрівна (фізико-математичні науки)
• Войнаш Віктор Зигфрідович (фізико-математичні науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"