Tkachenko M. V. Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics / M. V. Tkachenko, Z. Z. Zyman // Functional Materials. - 2008. - 15, № 4. - С. 574-579. - Бібліогр.: 12 назв. - англ.The carbonated hydroxyapatite powder was obtained by reaction of calcium carbonate with ortho-phosphoric acid. The compacted powder samples were sintered in the 800 - 1000 <$E symbol Р>C range in dry carbon dioxide atmosphere under atmospheric pressure. It is revealed that ceramics synthesized in such conditions is the AB type carbonated hydroxyapatite. The carbonization kind varies from mainly B type (at relatively low sintering temperatures) to mainly A type (at high ones). The carbonic gas atmosphere did not allow to suppress disintegration of a carbonated apatite at a sintering temperatures above 1100 <$E symbol Р>C, a partial decomposition of the B type apatite occurs with calcium oxide release. As a result, porosity of the ceramics increases and its mechanical properties drop sharply. However, at temperatures below 1100 <$E symbol Р>C, the carbon dioxide favors the activated shrinkage of compacts due to accelerated diffusion migration of the powder particles. In particular, the maximum density of ceramics (~ 94 % from the theoretical value) is reached at 1000 <$E symbol Р>C. Індекс рубрикатора НБУВ: Л420.7
Рубрики:
Шифр НБУВ: Ж41115 Пошук видання у каталогах НБУВ Додаткова інформація про автора(ів) публікації: (cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці) ![](/irbis_nbuv/images/info.png) Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"
|