Hysteretic Loops, 1,5; 3,0; 4,5; 6 and 10 nm in thickness, obtained by magnetron sputtering of Ni₈₁Fe₁₉ alloy, were measured by means of vibration magnetometer. It has been detected that by increasing the film thickness from 3 to 10 nm coercive force (HC) increases as well. In the direction perpendicular to the axis of easy magnetization the loop form considerably differs from the right-angled one, which is caused by amplitude dispersion of anisotropy. The films, derived in scattered magnetic field of the Earth, are by magnetic parameter isotropic. The results of atomic force microscope investigation indicate to the granular structure of films and confirms the presence of non-magnetized areas among the examined films. The critical thickness at which permalloy films pass from multi-domain to single-domain state was 10 nm. Estimation of the critical thickness of the transition from single-domain state to superparamagnetic led to the values of 1,5 - 2 nm.

 Наукова періодика України 

---

Додаткова інформація про автора(ів) публікації:
(cписок формується автоматично, до списку можуть бути включені персоналії з подібними іменами або однофамільці)

• Морозов Володимир Васильович (сільськогосподарські науки)

  Якщо, ви не знайшли інформацію про автора(ів) публікації, маєте бажання виправити або відобразити більш докладну інформацію про науковців України запрошуємо заповнити "Анкету науковця"